Please use this identifier to cite or link to this item: http://hdl.handle.net/2080/395
Full metadata record
DC FieldValueLanguage
dc.contributor.authorBera, T-
dc.contributor.authorMula, S-
dc.contributor.authorRay, P K-
dc.contributor.authorRay, B C-
dc.date.accessioned2007-01-08T09:39:36Z-
dc.date.available2007-01-08T09:39:36Z-
dc.date.issued2007-
dc.identifier.citationJournal of Reinforced Plastics and Composites, Vol 26, Iss 7, P 725-738en
dc.identifier.urihttp://hdl.handle.net/2080/395-
dc.descriptionCopyright for this article belongs to Sage. This is Author Version refreed post printen
dc.description.abstractThe aim of present study is to investigate the degradation behavior of glass fiber reinforced polyester composites during hygrothermal ageing for different lengths of time after suffering thermal shocks and thermal spikes at 1000C, 1500C, and 2000C. The moisture gain kinetics and change of interlaminar shear strength (ILSS), a primary mode of analysis of interfacial strength of the composite, were evaluated. Moisture absorption, found more in spiked samples, showed initial Fickian trend but eventually changed to non-linear pattern as the exposure time increased. It has been found that the composite specimens having a history of thermal spike showed more degradation. The damage was found even more at higher temperature and at lower loading rates.en
dc.format.extent231284 bytes-
dc.format.mimetypeapplication/pdf-
dc.language.isoen-
dc.publisherSageen
dc.subjectPolymer Matrix compositesen
dc.subjectDebondingen
dc.subjectEnvironmental Degradationen
dc.subjectInterfacial Strengthen
dc.subjectHygrothermal Behaviouren
dc.titleEffects of Thermal Shocks and Thermal Spikes on Hygrothermal Behavior of Glass-Polyester Compositesen
dc.typeArticleen
Appears in Collections:Journal Articles

Files in This Item:
File Description SizeFormat 
BCRAY-JRPC-2007-2.pdf225.86 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.