dc.identifier.citationPolymers and Polymer Composites, Vol 15, No 1, P 1-6en
dc.identifier.urihttp://hdl.handle.net/2080/302-
dc.descriptionCopyright for the published version belongs to Rapra. This is authors accepted post-print versionen
dc.description.abstractGlass fibres were used to fabricate epoxy and unsaturated polyester laminated composites, which were then immersed in seawater. The specimens were immediately transferred from one seawater bath to another one at a different temperature to induce thermal shock, with concurrent hydrothermal ageing. Thermal shocks of two types, up-cycle (lower to higher temperature immersion) and down-cycle (higher to lower temperature immersion) were applied and their repetition induced thermal fatigue. The aged samples were subjected to 3-point short beam shear tests. The tests were performed at room temperature with 2 mm/min and 50 mm/min crosshead speeds. The weakening effects were sensitive to loading rate. The effect of fibre volume fraction was also investigated. The maximum interlaminar shear strength fell by 35% in glass/epoxy composites (in 55 and 65 weight % fibres) and by 33% in glass/polyester composites (in 60 weight % fibres) as a result of the most severe conditioning cycles. It was also observed that the reduction in shear strength in general was less at high crosshead speeds. This may have been linked to a reduction in matrix ductility.en
dc.format.extent325015 bytes-
dc.format.mimetypeapplication/pdf-
dc.language.isoen-
dc.publisherRapraen
dc.subjectSeawater ageingen
dc.subjectmechanical behaviouren
dc.subjectpolymer compositesen
dc.subjectinterfaceen
dc.titleEffects of Changing Seawater Temperature on Mechanical Properties of GRP Compositesen
dc.typeArticleen
Appears in Collections:Journal Articles

Files in This Item:
File Description SizeFormat 
BCRAY-PPC-2006.pdf317.4 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.