Please use this identifier to cite or link to this item: http://hdl.handle.net/2080/2558
Full metadata record
DC FieldValueLanguage
dc.contributor.authorSaxena, R-
dc.contributor.authorPatra, A-
dc.contributor.authorKarak, S K-
dc.contributor.authorCiupinski, L-
dc.date.accessioned2016-11-15T07:14:20Z-
dc.date.available2016-11-15T07:14:20Z-
dc.date.issued2016-11-
dc.identifier.citation4th International Conference on Advances in Materials and Materials Processing (iCAMMP-IV), IIT Kharagpur, West Bengal, India, 5-7 November 2016en_US
dc.identifier.urihttp://hdl.handle.net/2080/2558-
dc.description.abstractThe present research work deals with fabrication of nano-Y2O3 dispersed tungsten (W) based alloys with nominal composition of W79Ni10Nb10(Y2O3)1 (alloy A), W78Ni10Nb10(Y2O3)2 (alloy B) and W72Ni10Nb15(Y2O3)3 (alloy C) (all composition in wt.%) by mechanical alloying in a planetary ball mill and compaction at 500 MPa pressure followed by sintering at 1500°C for 2 h in Ar atmosphere. The milled powders at different milling time and the consolidated products have been investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and energy dispersive spectroscopy (EDS). Minimum crystallite size and maximum lattice strain of 20.3 nm and 0.42% respectively is achieved in alloy C. Maximum sinterability, hardness, compressive strength of 93.38%, 6 GPa, 2.5 GPa with appreciable wear resistance has been achieved in alloy C owing to the lower crystallite size, presence of higher oxide dispersion (Y2O3) and NbNi intermetallic. High temperature behavior of the sintered alloys is studied in a raising hearth furnace at a temperature range of 800-1000°C. The activation energy of oxidation decreases with increase in Y2O3 content owing to higher energy of Y2O3 dispersoids. Alloy A shows superior oxidation resistance at 800-1000°C as compared to rest of the alloys. The investigated alloys shows superior strength and elongation as compared to recently investigated W-Y2O3 alloys [1, 2].en_US
dc.subjectW-Ni-Nb alloyen_US
dc.subjectMechanical alloyingen_US
dc.subjectOxide dispersion strengtheningen_US
dc.subjectHardnessen_US
dc.subjectOxidationen_US
dc.titleFabrication and Characterization of Nano–Y2O3 Dispersed Mechanically alloyed W-Ni-Nb for High Temperature Applicationsen_US
dc.typePresentationen_US
Appears in Collections:Conference Papers