Title: Loading Rate Effects on Mechanical Properties of Polymer Composites at Ultra-low Temperatures
Authors: Ray, B C
Keywords: Composites
Mechanical Properties
Failure
Fracture
Shear
Ultra-low Temperature
Issue Date: 2006
Publisher: Wiley Interscience
Citation: Journal of Applied Polymer Science, Vol 100, Iss 3, P 2289-2292
Abstract: E-glass fibers of 55, 60 and 65 weight percentages were reinforced with epoxy matrix to prepare the laminated composites. They were exposed to −40°C, −60°C, and −80°C temperatures for different times. The 3-pont bend test was conducted on the conditioned samples at those temperatures. Mechanical test was carried out at 2 mm/min and 500 mm/min crosshead speeds. The main emphasis of the investigation was to evaluate the roles of percentage matrix phase and interfacial areas on the interlaminar shear failure mechanism of glass/epoxy composites at ultra-low temperatures for different loading speeds. The mechanical performances of the laminated specimens at low temperatures were compared with room temperature property. The loading rate sensitivity of the polymer composites was appeared to be inconsistent and contradictory at some points of conditioning time and as well as at a temperature of conditioning. Phenomena may be attributed by low-temperature hardening, matrix cracking, misfit stra...
Description: Copyright for this article belongs to Wiley Interscience
URI: http://hdl.handle.net/2080/128
Appears in Collections:Journal Articles

Files in This Item:

File Description SizeFormat
bcray11.pdf1182KbAdobe PDFView/Open

Show full item record

All items in DSpace are protected by copyright, with all rights reserved.

 

Powered by DSpace Feedback