Title: | Low-Temperature Processing of Dense Hydroxyapatite-Zirconia Composites |
Authors: | Nayak, Y Rana, R Pratihar, S K Bhattacharyya, S |
Issue Date: | 2008 |
Publisher: | Blackwell |
Citation: | International Journal of Applied Ceramic Technology, Vol 5, No 1, P 29-36 |
Abstract: | Hydroxyapatite (HA)-YTZP (2, 5, 7.5, and 10 wt% ZrO2) composite powders prepared from inorganic precursors were characterized by FTIR, DSC/TG, XRD, and TEM. The calcined powders had HA and t/c-ZrO2, which undergo structural changes between 650°C and 1050°C. TEM of calcined powder showed larger HA particles (100 nm) and smaller ZrO2 particles (≤50 nm). HA and HA-2 wt% ZrO2-sintered samples had 98% density and it was (90-95%) for HA-5, 7.5, and 10 wt% ZrO2. The bending strength of HA-2wt% ZrO2 composites was 72 MPa. The grain sizes of HA showed a refinement with ZrO2 addition. |
Description: | Copyright for the article belongs to Blackwell |
URI: | http://dx.doi.org/10.1111/j.1744-7402.2008.02180.x http://hdl.handle.net/2080/646 |
Appears in Collections: | Journal Articles |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
pratihar-jact.pdf | 790.79 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.