http://hdl.handle.net/2080/454| Title: | Electrical Properties of Undoped and Lanthanum Doped a1Ti0.6Zro.403 |
| Authors: | Dash, M S Bera, J Ghosh, S |
| Issue Date: | 2006 |
| Publisher: | IEEE |
| Citation: | IEEE International Conference on Industrial Technology, ICIT, 15-17 Dec 2006 |
| Abstract: | Lanthanum doped BaTi0.6Zr0.4O3 composition x = 0.005, 0.01, 0.02, 0.05 and 0.1 in Ba1-xLaxTi0.6[1-5x/12]Zr0.4O3 were prepared by modified chemical route. (COOH)2.2H2O, Ba(NO3)2, ZrOCl2.8H2O and La2O3 are used to precipitate barium oxalate hydrate, lanthanum oxalate hydrate and zirconium oxy-hydroxide from its water solution onto the surface of suspended TiO2 particles. The lanthanum doped BaTi0.6Zr0.4O3 composition was found to be cubic by XRD analysis. A gradual shift of 2¿ angles to the higher angle with increasing lanthanum percentage in the BTZ reveals the contraction of perovskite lattice. The frequency dependence of dielectric permittivity and loss tan ¿ of the ceramics has been investigated. It is found that dielectric permittivity (¿r) decreases and loss tan ¿ decreases with increase in lanthanum percentage. Neither of the samples shows semiconductivity, which is believed to be because of titanium vacancy compensation. |
| Description: | Copyright for this article belongs to IEEE DOI:10.1109/ICIT.2006.372695 |
| URI: | http://hdl.handle.net/2080/454 |
| Appears in Collections: | Conference Papers |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| IEEE ICIT 04238017 INDIA 2006.pdf | 3.71 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.