Title: | Effect of Cure Kinetics and Addition of Various Nanomaterials on Glass Fiber/Vinyl Ester Composites |
Authors: | Yadav, Avadesh Ganesh Gupta K, B N V S Fulmali, Abhinav Omprakash Prusty, Rajesh Kumar Ray, B C |
Keywords: | Glass fiber/Vinyl ester composites Nanomaterials Solution processing Mechanical Testing |
Issue Date: | Dec-2019 |
Citation: | International Conference on Processing and Characterization of Materials (ICPCM-2019), National Institute of Technology, Rourkela, 12th-14th December 2019 |
Abstract: | In this article, optimization of post-cure temperature for glass fiber/vinyl ester (GVE) composite at 80°C, 110°C and 140°C for 6 hr was studied. Mechanical strength and glass transition temperature (Tg) of GVE composites reinforced with 0.1 wt.% of various nanofillers such as carboxyl functionalized multi-walled carbon nanotube (CNT-COOH), nanoclay (surface-modified), nano alumina (Al2O3) and nano silica (SiO2) was investigated. Optimum properties for GVE composite were obtained at 140°C post-cure temperature. With the incorporarion of nanomaterials, flexural properties were improved whereas significant improvement acquired in the case of nanoclay GVE composite with a optimum flexural strength of 381.16 MPa and Tg of 102°C. Post failure analysis of the tested samples was studied using a scanning electron microscope (SEM) at room temperature. |
Description: | Copyright belongs to proceeding publisher |
URI: | http://hdl.handle.net/2080/3468 |
Appears in Collections: | Conference Papers |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
2019_ICPCM_AYadav_Effect.pdf | 816.62 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.