Please use this identifier to cite or link to this item: http://hdl.handle.net/2080/2641
Full metadata record
DC FieldValueLanguage
dc.contributor.authorDash, Smaranika-
dc.contributor.authorMohanty, H S-
dc.contributor.authorKumar, Ashok-
dc.contributor.authorSen, Shrabanee-
dc.contributor.authorPradhan, Dillip Kumar-
dc.date.accessioned2017-02-09T10:02:38Z-
dc.date.available2017-02-09T10:02:38Z-
dc.date.issued2016-11-
dc.identifier.citationInternational Conference on Technologically Advanced Materials & Asian Meeting on Ferroelectricity(ICTAM-AMF10), New Delhi, Delhi, India, 7-11 November 2016en_US
dc.identifier.urihttp://hdl.handle.net/2080/2641-
dc.description.abstractThe lead free polycrystalline ferroelectric samples of 0.45Ba(Zr0.2Ti0.8 ) O3 -0.55(Ba0.7 Ca0.3 )TiO3 have been synthesized by auto combustion technique. The room temperature XRD pattern reveals the formation of single phase compound. The temperature dependent dielectric measurement for both poled and unpoled sample has been carried out. The temperature dependent dielectric properties shows a high dielectric constant (ɛr ) value of 5880 around Tc =95 0C (for poled) and 5869 around Tc =89 0C ( for unpoled) sample. The I-V characteristic shows a symmetric behaviour for both positive and negative applied electric field. The sample shows a saturated ferroelectric behaviour for both poled and unpoled case. From P-E hysteresis loop, the remnant polarisation (2Pr 0 ) and coercive field (Ec 0 ) for are found to be 5.39μC/cm2 , 4.672 kV/cm (poled sample ) and 3.44 μC/cm2 , 3.893 kV/cm (unpoled sample ) respectively.en_US
dc.subjectPolycrystalline ferroelectricen_US
dc.subjectPolar Natureen_US
dc.subjectXRD Patternen_US
dc.titlePolar Nature of (1-x) Ba(Zr0.2Ti0.8 )O3 - x (Ba0.7Ca0.3 )TiO3 ceramic Near Morphotropic Phase Boundaryen_US
dc.typePresentationen_US
Appears in Collections:Conference Papers