Title: | Mechanical Behavior and Microstructural Characterization of ZrB2-B4C-Mo Cermets Synthesized by Ball Milling |
Authors: | Rout, R R Mishra, B Sahoo, N Karak, S K |
Keywords: | Cermet Hydraulic Hardness Wear Densification Metastable |
Issue Date: | Nov-2016 |
Citation: | 4th International Conference on Advances in Materials and Materials Processing (iCAMMP-IV), IIT Kharagpur, West Bengal, India, 5-7 November 2016 |
Abstract: | The present paper deals with the study of mechanical behavior of ZrB2-B4C-Mo cermets where optimal composition consisting of ZrB2, B4C and Mo are respectively in proportion of 40, 40 and 20 (all in wt. %). For comparative study, the firing of cermest was done at 1500⁰C, 1600⁰C for 2hrs & 1800⁰C for 3 min in reducing atmosphere .The Vickers hardness test of the cermet fired at 1500⁰C & 1600⁰C shows hardness of 16GPa & 18GPa respectively whereas sample fired at 1800⁰C shows 32GPa. Similarly wear depth of sample fired at 1500⁰C & 1600⁰C shows higher mass loss than that of sample fired at 1800⁰C.This may be attributed to the formation of metastable phases like MoB, ZrC which densify the structure at 1800⁰C and strengthen the whole matrix. |
URI: | http://hdl.handle.net/2080/2562 |
Appears in Collections: | Conference Papers |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
2016_ICAMMP_SKKarak_Mechanical.pdf | 6.72 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.