Title: | Thermal and In-vitro Study of Borate Based Bioglass |
Authors: | Pal, S K Banerjee, I Singh, S Chakraborty, S |
Keywords: | Bioglass Boron Mineralization Osteo-conductive |
Issue Date: | Sep-2015 |
Citation: | International Commission on Glass (ICG) Annual Meeting 2015 , Bangkok, Thailand, 20-23 September 2015 |
Abstract: | Bio-glasses have drawn attention of engineers and scientists in the field of bone tissue engineering filed due to its versatile properties than other Bioceramics such as ability to form bond with soft and hard tissues. Therefore, bio-glasses are considered as one of the promising materials for preparing three-dimensional porous scaffold, which can mimic the natural bone structure. In this regard, the bioglass 45S5 (discovered by Larry Hench 1960) was subject for intense research for decades and research is still continuing even after successful commercialization. But there is always search for new bioglass composition to overcome some hurdles like superior mechanical properties, controlled degradation rate and to find new functionality in the field of biomedical research. Borate based bioglass are comparative new class of bioglass in this this regard. In some resent work it has been reported that borate based bioglass can show better bioactivity than silicate based glass. But not much has been reported with respect to mechanical properties, thermal behavior as well as bioactivity of borate based bioglass. In the present work three different 20B2O3-80(CaO- P2O5) (in weight percentage) frit glasses has been prepared by traditional melt quenching method. In these compositions Ca:P ratio was varied (1.65, 1.67 and 1.69) to investigate the effect of Ca:P ratin on thermal and in vitro biological properties of these glass. As these glasses are prone to crystallization at high temperature, therefore, crystallization behavior of all glasses has been investigated through DSC analysis. For scaffold preparation, the frit glasses need to be sintered at high temperature. Dilatometric studies have also been carried out to examine the sintering behavior. Porous Scaffolds have been prepared using naphthalene as pore former which is followed by sintering. The porosity and pore morphology has been studied using Mercury Porosimetry. Mechanical properties of porous as well as no porous glasses have also been measured through 3-point bending method and Brazilian Disc Test Method. The mineralization behavior of glass frit as well as glass scaffold has been tested by immersing the samples in SBF solution and examining them after 1, 3, 7, 14, 21 and 28 days. Mineralization behavior has been examined through XRD analysis and microstructure of deposited HCA layer has been examined through FESEM. Osteo-conductive property of the samples was tested using human osteoblast cell line (MG-63) in vitro. Initial cell- bioglass interaction has been evaluated in terms of cell adhesion and cell spreading using (immune-cytochemistry). Effect of the samples on cell viability and proliferation has been tested using MTT assay and cell cycle analysis. Influence of the biomaterial on the differentiation of the bone cells were further tested by checking the expression of differentiation marker like Runx2. For the whole study commercial hydroxy apatite has taken as control. Study has revealed that the newly developed borate bioglasses are highly biocompatible and osteo-conductive in nature. |
URI: | http://hdl.handle.net/2080/2373 |
Appears in Collections: | Conference Papers |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
skpal_thermal_2015.pdf | 2.93 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.