Title: | Recrystallization Texture in Commercially Pure (CP) Titanium |
Authors: | Panda, S Kumar, G Mishra, S C Suwas, S Sahoo, S K |
Issue Date: | Aug-2014 |
Citation: | 17th International Conference on Textures of Materials, August 24 - 29, 2014, Dresden |
Abstract: | Texture development during annealing of commercial pure titanium (cp-titanium) was extensively studied. Cp-titanium plates were subjected to rolling, accumulative roll bonding (ARB) and cross-rolling in a laboratory rolling mill. Rolling and cross-rolling was carried out till 90% reduction of thickness while ARB processing was done for six passes. The rolled sheets were then subjected to annealing for a large-range of soaking times starting from 10s to 30 min. The samples were fully annealed after 5 min of annealing, as measured by electron backscattered diffraction. The texture development was different in rolled, ARB processed and cross-rolled samples before annealing. However, beyond 5 min of annealing time the texture was almost similar in all the samples. It was also observed that the texture development was insignificant in ARB processed samples during annealing. |
Description: | Copyright for this presentation belongs to proceeding publisher |
URI: | http://hdl.handle.net/2080/2178 |
Appears in Collections: | Conference Papers |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
icotom-17.pdf | 3.66 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.