Title: | Loading Rate Effects on Mechanical Properties of Polymer Composites at Ultra-low Temperatures |
Authors: | Ray, B C |
Keywords: | Composites Mechanical Properties Failure Fracture Shear Ultra-low Temperature |
Issue Date: | 2006 |
Publisher: | Wiley Interscience |
Citation: | Journal of Applied Polymer Science, Vol 100, Iss 3, P 2289-2292 |
Abstract: | E-glass fibers of 55, 60 and 65 weight percentages were reinforced with epoxy matrix to prepare the laminated composites. They were exposed to −40°C, −60°C, and −80°C temperatures for different times. The 3-pont bend test was conducted on the conditioned samples at those temperatures. Mechanical test was carried out at 2 mm/min and 500 mm/min crosshead speeds. The main emphasis of the investigation was to evaluate the roles of percentage matrix phase and interfacial areas on the interlaminar shear failure mechanism of glass/epoxy composites at ultra-low temperatures for different loading speeds. The mechanical performances of the laminated specimens at low temperatures were compared with room temperature property. The loading rate sensitivity of the polymer composites was appeared to be inconsistent and contradictory at some points of conditioning time and as well as at a temperature of conditioning. Phenomena may be attributed by low-temperature hardening, matrix cracking, misfit strain due to differential thermal coefficient of the constituent phases and also by enhanced mechanical keying factor by compressive residual stresses at low temperatures. |
Description: | Copyright for this article belongs to Wiley Interscience |
URI: | http://hdl.handle.net/2080/128 |
Appears in Collections: | Journal Articles |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
bcray11.pdf | 1.18 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.