dc.identifier.citationTransactions of the Indian Ceramic Society, Volume 68, No 2, Pages 1-4, 2009en
dc.identifier.urihttp://hdl.handle.net/2080/1037-
dc.description.abstractSilica aerogel was prepared from rice husk ash by sol-gel process followed by ambient pressure drying. Silica was extracted from ash as sodium silicate by boiling it in sodium hydroxide solution.Sodium silicate was neutralized with nitric acid to form silica gel. To prepare aerogel, first the pore water of the gel was exchanged by ethanol and then surface modification was done by aging alcogel in tetraethylorthosilicate (TEOS)/ethanol solution. Before drying, TEOS/ethanol solvent was exchanged with n-heptane. Capillary stress and shrinkages were greatly reduced due to the low surface tension of n-heptane. The prepared aerogel was a light and crack-free solid, with bulk density of 0.67 g.cm–3,porosity of about 80%, total pore volume of 3.1 cm3.g–1 and specific surface area of about 273 m2.g–1. The nature of surface modification and thermal stability of the aerogel was studied by FTIR and DSC/TG respectively.en
dc.format.extent444136 bytes-
dc.format.mimetypeapplication/pdf-
dc.language.isoen-
dc.publisherThe Indian Ceramic Societyen
dc.subjectSilica aerogelen
dc.subjectRice husk ashen
dc.subjectAmbient pressure dryingen
dc.titlePreparation of Silica Aerogel by Ambient Pressure Drying Process using Rice Husk Ash as Raw Materialen
dc.typeArticleen
Appears in Collections:Journal Articles

Files in This Item:
File Description SizeFormat 
preparation.pdf433.73 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.