DC FieldValueLanguage
contributor.authorBera, J-
contributor.authorRoy, P K-
date.accessioned2005-06-04T08:03:54Z-
date.available2005-06-04T08:03:54Z-
date.issued2005-06-15-
identifier.citationPhysica B: Condensed Matter, Vol 363, Iss 1-4, P 128-132en
identifier.urihttp://hdl.handle.net/2080/49-
descriptionCopyright of this article belongs to Elsevier Science Ltd Link: doi:10.1016/j.physb.2005.03.010en
description.abstractThe electromagnetic properties of polycrystalline Ni0.7Zn0.3Fe2O4 with varying grain size in the range 1–12 μm, were investigated. The grain size was varied by sintering the ferrite at different temperatures/time upto 1300 °C/240 min. A rapid grain growth was observed at 1300 °C/240 min. Initial permeability was found to increase linearly with the grain size upto about 5 μm and after that the rate of increase was reduced due to the formation of more number of closed porosity. The permeability and relative loss factor were very stable upto about 10 MHz in small-grained cores. A relatively lower loss factor in the order of 10−5 was found in the material. Resistivity was found to decrease sharply with the grain size. The ferrite with 1250 °C/60 min firing was best for high-frequency low-loss applicationen
format.extent163653 bytes-
format.mimetypeapplication/pdf-
language.isoen-
publisherElsevieren
subjectElectroceramicsen
subjectFerritesen
subjectGrain sizeen
subjectPermeabilityen
subjectResistivityen
titleEffect of grain size on electromagnetic properties of Ni0.7Zn0.3Fe2O4 ferriteen
typeArticleen
Appears in Collections:Journal Articles
Journal Articles

Files in This Item:

File Description SizeFormat
bera5.pdf159KbAdobe PDFView/Open

Show simple item record

All items in DSpace are protected by copyright, with all rights reserved.

 

Powered by DSpace Feedback